Resorbable magnesium metal membrane for sinus lift procedures: a case series.

BACKGROUND: The purpose of this case series was to demonstrate the use of a magnesium membrane for repairing the perforated membrane in both direct and indirect approaches, as well as its application in instances where there has been a tear of the Schneiderian membrane. CASE PRESENTATION: The case series included four individual cases, each demonstrating the application of a magnesium membrane followed by bone augmentation using a mixture of xenograft and allograft material in the sinus cavity. In the first three cases, rupture of Schneiderian membrane occurred as a result of tooth extraction, positioning of the dental implant, or as a complication during the procedure. In the fourth case, Schneiderian membrane was perforated as a result of the need to aspirate a polyp in the maxillary sinus. In case one, 10 mm of newly formed bone is visible four months after graft placement. Other cases showed between 15 and 20 mm of newly formed alveolar bone. No residual magnesium membrane was seen on clinical inspection. The vertical and horizontal augmentations proved stable and the dental implants were placed in the previously grafted sites. CONCLUSION: Within the limitations of this case series, postoperative clinical examination, and panoramic and CBCT images demonstrated that resorbable magnesium membrane is a viable material for sinus lift and Schneiderian membrane repair. The case series showed successful healing and formation of new alveolar bone with separation of the oral cavity and maxillary sinus in four patients.

Regeneration of Intrabony Defects Using a Novel Magnesium Membrane.

Background and Objectives: Due to their specific morphology, the regeneration of intrabony defects (IBDs) represents one of the greatest challenges for clinicians. Based on the specific properties of a magnesium membrane, a new approach for the surgical treatment of IBD was developed. The surgical procedure was described using a series of three cases. Materials and Methods: The patients were healthy individuals suffering from a severe form of periodontitis associated with IBD. Based on radiographic examination, the patients had interproximal bone loss of at least 4 mm. Due to its good mechanical properties, it was easy to cut and shape the magnesium membrane into three different shapes to treat the specific morphology of each IBD. In accordance with the principles of guided bone regeneration, a bovine xenograft was used to fill the IBD in all cases. Results: After a healing period of 4 to 6 months, successful bone regeneration was confirmed using radiological analysis. The periodontal probing depth (PPD) after healing showed a reduction of 1.66 ± 0.29 mm. Conclusions: Overall, the use of the different shapes of the magnesium membrane in the treatment of IBD resulted in a satisfactory functional and esthetic outcome.

Possible Applications for a Biodegradable Magnesium Membrane in Alveolar Ridge Augmentation-Retrospective Case Report with Two Years of Follow-Up.

Background and Objectives: A rigid, resorbable magnesium membrane was recently developed, combining the advantages of resorbable and non-resorbable membranes. Our aim was to describe the application of this membrane for guided bone regeneration (GBR). Materials and Methods: This case report described the treatment and 3D evaluation of two cases utilizing a resorbable magnesium barrier membrane. In Case #1, GBR was performed with a bilayer tunnel flap. The magnesium barrier was placed fixed subperiosteally through remote vertical incisions. In Case #2, GBR was performed using a split-thickness flap design. Volumetric and linear hard tissue alterations were assessed by 3D cone-beam computed tomography subtraction analysis, as well as with conventional intraoral radiography. Results: Case #1 showed a volumetric hard tissue gain of 0.12 cm3, whereas Case #2 presented a 0.36 cm3 hard tissue gain. No marginal peri-implant hard tissue loss could be detected at the two-year follow-up. Conclusions: The application of conventional resorbable collagen membranes would be difficult in either of the cases presented. However, the rigid structure of the magnesium membrane allowed for the limitations of conventional resorbable membranes to be overcome.

Regeneration of Buccal Wall Defects after Tooth Extraction with Biphasic Calcium Phosphate in Injectable Form vs. Bovine Xenograft: A Randomized Controlled Clinical Trial.

Bone healing after tooth extraction may be affected by defects of the alveolus buccal wall, such as fenestrations and dehiscences. Therefore, to minimize dimensional changes it is advisable to perform alveolar ridge preservation after tooth extractions. Different biomaterials are used for this purpose. The aim of this study was to investigate the qualitative and quantitative histological changes in human biopsies taken after 6 months of healing of extraction sockets with buccal wall defects. For this purpose, the defects of 36 patients (18 per group) were treated with injectable biphasic calcium phosphate (I-BCP) or bovine xenograft (BX) after extraction. After six months of healing, biopsies were taken and proceeded to the histology laboratory. No evidence of an inflammatory response of the tissue was observed in the biopsies of either group, and the newly formed bone (NB) was in close contact with the remaining biomaterial (BM). The histomorphometric results showed that there was no statistically significant difference between the groups in the mean percentage of NB (p = 0.854), BM (p = 0.129), and soft tissue (p = 0.094). To conclude, both biomaterials exhibited osteoconductivity and biocompatibility and achieved satisfactory bone regeneration of buccal wall defects after tooth extraction.

Evaluation between Biodegradable Magnesium Metal GBR Membrane and Bovine Graft with or without Hyaluronate.

Bone substitutes and barrier membranes are widely used in dental regeneration procedures. New materials are constantly being developed to provide the most optimal surgical outcomes. One of these developments is the addition of hyaluronate (HA) to the bovine bone graft, which has beneficial wound healing and handling properties. However, an acidic environment that is potentially produced by the HA is known to increase the degradation of magnesium metal. The aim of this study was to evaluate the potential risk for the addition of HA to the bovine bone graft on the degradation rate and hence the efficacy of a new biodegradable magnesium metal GBR membrane. pH and conductivity measurements were made in vitro for samples placed in phosphate-buffered solutions. These in vitro tests showed that the combination of the bovine graft with HA resulted in an alkaline environment for the concentrations that were used. The combination was also tested in a clinical setting. The use of the magnesium metal membrane in combination with the tested grafting materials achieved successful treatment in these patients and no adverse effects were observed in vivo for regenerative treatments with or without HA. Magnesium based biodegradable GBR membranes can be safely used in combination with bovine graft with or without hyaluronate.

Alteration of Collagen Content and Macrophage Distribution in White Adipose Tissue under the Influence of Maternal and Postnatal Diet in Male Rat Offspring.

Background and Objectives: The extracellular matrix is important for adipose tissue growth, and numerous interactions between adipocytes and extracellular matrix components occur during adipose tissue development. The main objective of this study was to investigate the interaction and influence of maternal and postnatal diet on adipose tissue remodeling in Sprague Dawley offspring. Materials and Methods: 10 Sprague Dawley females were randomly divided into two groups at nine weeks of age and fed a standard laboratory diet or high-fat diet for six weeks. Then, they were mated, and after birth, their male rat offspring were divided into four subgroups according to diet. After euthanizing the offspring at 22 weeks of age, samples of subcutaneous, perirenal and epididymal adipose tissue were collected. Sections were stained with Mallory's trichrome and analyzed by immunohistochemistry for CD68+ and CD163+ cells. Results: Staining of extracellular components showed higher collagen deposition in the perirenal and epididymal depot of offspring fed a high-fat diet. The number of CD163/CD68+ cells in the perirenal adipose tissue was lower in the CD-HFD group compared with other groups, and in the subcutaneous fat pad when the groups with modified diet were compared with those on non-modified diet. Conclusion: Morphological changes in adipose tissue, increased collagen deposition, and changes in macrophage polarization may be related to intergenerational changes in diet.

A Histologic, Histomorphometric, and Immunohistochemical Evaluation of Anorganic Bovine Bone and Injectable Biphasic Calcium Phosphate in Humans: A Randomized Clinical Trial.

Following trauma, chronic periapical process, or tooth extraction, a large loss of bone volume is noticed during the healing process. To facilitate the placement of dental implants, various surgical procedures are used for an optimal alveolar ridge profile, while maintaining adequate bone dimensions. The main aim of this study was to determine the healing ability (histologically and immunohistologically) of alveolar bone defects during augmentation with two different biomaterials: injectable biphasic calcium phosphate (BCP) and anorganic bovine bone (ABB). Thirty-eight subjects were randomly divided into two groups. The first group received the tested bone substitute biomaterial (BSB), i.e., BCP (maxresorb inject®), and the second group received an alternative to the gold standard, i.e., ABB (Bio-Oss®). The histopathological, histomorphometric, and immunohistochemical analyses gave comparable results for these bone substitute materials in terms of newly formed bone: (BCP: 39.91 ± 8.49%, ABB: 41.73 ± 13.99%), residual biomaterial (BCP: 28.61 ± 11.38%, ABB: 31.72 ± 15.52%), and soft tissue (BCP: 31.49 ± 11.09%, ABB: 26.54 ± 7.25%), with no significant difference found between the groups (p < 0.05, t-test), proving that BCP is equally suitable and successful for alveolar bone regeneration.

Application of Biodegradable Magnesium Membrane Shield Technique for Immediate Dentoalveolar Bone Regeneration.

For the first time, the clinical application of the first CE registered magnesium membrane is reported. Due to the material characteristics of magnesium metal, new treatment methodologies become possible. This has led to the development of a new technique: the magnesium membrane shield technique, used to rebuild the buccal or palatal walls of compromised extraction sockets. Four clinical cases are reported, demonstrating the handling options of this new technique for providing a successful regenerative outcome. Using the technique, immediate implant placement is possible with a provisional implant in the aesthetic zone. It can also be used for rebuilding both the buccal and palatal walls simultaneously. For instances where additional mechanical support is required, the membrane can be bent into a double layer, which additionally provides a rounder edge for interfacing with the soft tissue. In all reported clinical cases, there was a good bone tissue regeneration and soft tissue healing. In some instances, the new bone had formed a thick cortical bone visible in cone beam computed tomography (CBCT) radiographs of the regenerated sites, which is known to be remodeled in the post treatment period. Overall, the magnesium membrane shield technique is presented as an alternative treatment option for compromised extraction sockets.

Biodegradation of a Magnesium Alloy Fixation Screw Used in a Guided Bone Regeneration Model in Beagle Dogs.

Nowadays, the most commonly used fixation systems are non-resorbable, but new resorbable magnesium alloy fixation screws have been introduced recently. Therefore, the aim of this study was to compare the magnesium fixation screw and the commonly used non-resorbable titanium screw in an animal model. Four 3-wall defect sites were covered with collagen membranes in the mandible of twenty beagle dogs (two sites on the left and two on the right). Each membrane was fixed with either four magnesium screws or four titanium screws. Post-operative follow-up revealed the expected observations such as transient inflammation and pain. Both groups showed a good healing response, with no differences between groups. Micro-CT analysis showed no significant difference between groups in terms of BV/TV or soft tissue volume. The void volume in the magnesium fixation screw group continued to decrease on average between the different timepoints, but not significantly. Furthermore, a gradual progression of the degradation process of the magnesium screws was observed in the same group. Magnesium screws and titanium screws showed equal performance in tissue regeneration according to GBR principles. An additional advantage of magnesium screws is their resorbable nature, which eliminates the need for a second surgical step to remove the screws.

Analysis of a Pure Magnesium Membrane Degradation Process and Its Functionality When Used in a Guided Bone Regeneration Model in Beagle Dogs.

For the surgical technique of guided bone regeneration (GBR), the choice of available barrier membranes has until recently not included an option that is mechanically strong, durable, synthetic and resorbable. The most commonly used resorbable membranes are made from collagen, which are restricted in their mechanical strength. The purpose of this study is to evaluate the degradation and regeneration potential of a magnesium membrane compared to a collagen membrane. In eighteen beagle dogs, experimental bone defects were filled with bovine xenograft and covered with either a magnesium membrane or collagen membrane. The health status of the animals was regularly monitored and recorded. Following sacrifice, the hemimandibles were prepared for micro-CT (µ-CT) analysis. Complications during healing were observed in both groups, but ultimately, the regenerative outcome was similar between groups. The µ-CT parameters showed comparable results in both groups in terms of new bone formation at all four time points. In addition, the µ-CT analysis showed that the greatest degradation of the magnesium membranes occurred between 1 and 8 weeks and continued until week 16. The proportion of new bone within the defect site was similar for both treatment groups, indicating the potential for the magnesium membrane to be used as a viable alternative to collagen membranes. Overall, the new magnesium membrane is a functional and safe membrane for the treatment of defects according to the principles of GBR.

Biodegradable magnesium barrier membrane used for guided bone regeneration in dental surgery.

Barrier membranes are commonly used as part of the dental surgical technique guided bone regeneration (GBR) and are often made of resorbable collagen or non-resorbable materials such as PTFE. While collagen membranes do not provide sufficient mechanical protection of the covered bone defect, titanium reinforced membranes and non-resorbable membranes need to be removed in a second surgery. Thus, biodegradable GBR membranes made of pure magnesium might be an alternative. In this study a biodegradable pure magnesium (99.95%) membrane has been proven to have all of the necessary requirements for an optimal regenerative outcome from both a mechanical and biological perspective. After implantation, the magnesium membrane separates the regenerating bone from the overlying, faster proliferating soft tissue. During the initial healing period, the membrane maintained a barrier function and space provision, whilst retaining the positioning of the bone graft material within the defect space. As the magnesium metal corroded, it formed a salty corrosion layer and local gas cavities, both of which extended the functional lifespan of the membrane barrier capabilities. During the resorption of the magnesium metal and magnesium salts, it was observed that the membrane became surrounded and then replaced by new bone. After the membrane had completely resorbed, only healthy tissue remained. The in vivo performance study demonstrated that the magnesium membrane has a comparable healing response and tissue regeneration to that of a resorbable collagen membrane. Overall, the magnesium membrane demonstrated all of the ideal qualities for a barrier membrane used in GBR treatment.

Biodegradable magnesium fixation screw for barrier membranes used in guided bone regeneration.

An ideal fixation system for guided bone (GBR) regeneration in oral surgery must fulfil several criteria that includes the provision of adequate mechanical fixation, complete resorption when no longer needed, complete replacement by bone, as well as be biocompatible and have a good clinical manageability. For the first time, a biodegradable magnesium fixation screw made of the magnesium alloy WZM211 with a MgF2 coating has been designed and tested to fulfill these criteria. Adequate mechanical fixation was shown for the magnesium fixation screw in several benchtop tests that directly compared the magnesium fixation screw with an equivalent polymeric resorbable device. Results demonstrated slightly superior mechanical properties of the magnesium device in comparison to the polymeric device even after 4 weeks of degradation. Biocompatibility of the magnesium fixation screw was demonstrated in several in vitro and in vivo tests. Degradation of the magnesium screw was investigated in in vitro and in vivo tests, where it was found that the screw is resorbed slowly and completely after 52 weeks, providing adequate fixation in the early critical healing phase. Overall, the magnesium fixation screw demonstrates all of the key properties required for an ideal fixation screw of membranes used in guided bone regeneration (GBR) surgeries.

Biocompatibility Analyses of HF-Passivated Magnesium Screws for Guided Bone Regeneration (GBR).

Background: Magnesium (Mg) is one of the most promising materials for human use in surgery due to material characteristics such as its elastic modulus as well as its resorbable and regenerative properties. In this study, HF-coated and uncoated novel bioresorbable magnesium fixation screws for maxillofacial and dental surgical applications were investigated in vitro and in vivo to evaluate the biocompatibility of the HF coating. Methods: Mg alloy screws that had either undergone a surface treatment with hydrofluoric-acid (HF) or left untreated were investigated. In vitro investigation included XTT, BrdU and LDH in accordance with the DIN ISO 10993-5/-12. In vivo, the screws were implanted into the tibia of rabbits. After 3 and 6 weeks, degradation, local tissue reactions and bony integration were analyzed histopathologically and histomorphometrically. Additionally, SEM/EDX analysis and synchrotron phase-contrast microtomography (µCT) measurements were conducted. The in vitro analyses revealed that the Mg screws are cytocompatible, with improved results when the surface had been passivated with HF. In vivo, the HF-treated Mg screws implanted showed a reduction in gas formation, slower biodegradation and a better bony integration in comparison to the untreated Mg screws. Histopathologically, the HF-passivated screws induced a layer of macrophages as part of its biodegradation process, whereas the untreated screws caused a slight fibrous tissue reaction. SEM/EDX analysis showed that both screws formed a similar layer of calcium phosphates on their surfaces and were surrounded by bone. Furthermore, the µCT revealed the presence of a metallic core of the screws, a faster absorbing corrosion front and a slow absorbing region of corroded magnesium. Conclusions: Overall, the HF-passivated Mg fixation screws showed significantly better biocompatibility in vitro and in vivo compared to the untreated screws.

Peri-Implant Mucosa Augmentation with an Acellular Collagen Matrix.

Peri-implant keratinized mucosa (PI-KM) may support implant survival. Acellular collagen matrices (aCMs) have been widely used to facilitate soft tissue regeneration. The aim of this study was to investigate clinical outcomes obtained with the use of an aCM (mucoderm®) to enhance PI-KM. In this retrospective non-randomized case series, 27 restored implants in 14 patients (eight males and six females, mean age = 56 years) with a PI-KM width ≤ 1 mm were followed for 6 months. It was demonstrated that aCM grafts augmented PI-KM effectively (mean increase of 5.4 mm; >533%) without a significant change in bleeding on probing (BOP) from baseline. The mean aCM shrinkage was 3.9 mm (42%). Gender, area, arch, and BOP did not influence PI-KM augmentation or aCM shrinkage significantly. The present results demonstrated that the examined aCM was effective and predictable for attaining a band of keratinized tissue, while avoiding graft donor site harversting.

Open-Healing Socket Preservation with a Novel Dense Polytetrafluoroethylene (dPTFE) Membrane: A Retrospective Clinical Study.

Background and objectives: Non-resorbable dense polytetrafluoroethylene (dPTFE) membranes are widely used for regeneration procedures, alone or in combination with particulate materials. The aim of this work was to examine the efficacy of a newly developed dPTFE membrane in the management of extraction socket healing. Materials and Methods: The extraction premolar sockets of 44 patients (20 men and 24 women) were preserved. One group received prosthetic rehabilitation with a fixed partial denture (FPD) (PROS group, N = 19) and a second group received immediate implant placement (IMPL group, N = 25). The PROS group sockets were augmented with a bovine derived xenograft and covered with a newly developed dPTFE membrane prior to FPD rehabilitation. Results: In the IMPL group, socket preservation was combined with immediate implant placement. Before (T0) and 6 months after surgery (T1), horizontal and vertical dimensions were measured with customized stents. No significant differences in alveolar bone loss from T0 to T1 were observed between the PROS and IMPL groups in the horizontal dimension for any tooth type. There was a significant difference in alveolar bone loss from T0 to T1 between the two groups for only single-rooted maxillary premolars in the vertical dimension. Conclusions: The use of the examined new dPTFE membrane consistently led to the preservation of hard tissue in the extraction sites.

Additive Manufacturing for Guided Bone Regeneration: A Perspective for Alveolar Ridge Augmentation.

Three-dimensional (3D) printing has become an important tool in the field of tissue engineering and its further development will lead to completely new clinical possibilities. The ability to create tissue scaffolds with controllable characteristics, such as internal architecture, porosity, and interconnectivity make it highly desirable in comparison to conventional techniques, which lack a defined structure and repeatability between scaffolds. Furthermore, 3D printing allows for the production of scaffolds with patient-specific dimensions using computer-aided design. The availability of commercially available 3D printed permanent implants is on the rise; however, there are yet to be any commercially available biodegradable/bioresorbable devices. This review will compare the main 3D printing techniques of: stereolithography; selective laser sintering; powder bed inkjet printing and extrusion printing; for the fabrication of biodegradable/bioresorbable bone tissue scaffolds; and, discuss their potential for dental applications, specifically augmentation of the alveolar ridge.

Bioprinting of tissue engineering scaffolds.

Bioprinting is the process of creating three-dimensional structures consisting of biomaterials, cells, and biomolecules. The current additive manufacturing techniques, inkjet-, extrusion-, and laser-based, create hydrogel structures for cellular encapsulation and support. The requirements for each technique, as well as the technical challenges of printing living cells, are discussed and compared. This review encompasses the current research of bioprinting for tissue engineering and its potential for creating tissue-mimicking structures.

Different combinations of maternal and postnatal diet are reflected in changes of hepatic parenchyma and hepatic TNF-alpha expression in male rat offspring.

Obesity is related to increased TNF-alpha production in different tissues. TNF-alpha is connected to mitochondrial dysfunction in the liver and also development of fatty infiltration of the liver. Also, postnatal change from normal to high-fat diet causes a significant increase in TNF-alpha serum levels. The aim of this research was to determine how maternal diet and switching male offspring to a different dietary regime after lactation influences rat liver. Ten female Sprague Dawley rats at nine weeks of age were randomly divided in two groups and fed either standard laboratory chow or high-fat diet during six weeks, and then mated with the same male subject. After birth and lactation male offspring from both groups were further divided into four subgroups depending on their subsequent diet. At 22 weeks of age, the animals were weighted, sacrificed and major organs were collected and weighted. Immunohistochemistry for TNF-alpha was performed on liver, and liver samples were analyzed for pathohistological changes. The group in which mothers were fed standard chow and offspring high-fat diet had the most pronounced changes: heaviest liver, poorest histopathological findings and strongest TNF-alpha immunohistochemical staining of liver parenchyma. High-fat diet during pregnancy and lactation and switching to high-fat diet postnatally affects liver weight, histological structure and TNF-alpha expression in male offspring.

Effects of between generations changes in nutrition type on vaginal smear and serum lipids in Sprague-Dawley rats.

OBJECTIVE: Previous studies established that between generations changes in feeding protocol can have significant impact on reproductive physiology. The aim of the study was to determinate effects of mothers' nutrition and nutrition of the offspring on the characteristics of vaginal smear and serum lipid content. METHODS: Ten female rats were randomly divided in two groups; first group fed with food containing high content of saturated fatty acids (HFD) and the second with standard laboratory chow (CD). After coupling and lactation period their offspring were further randomly divided into two subgroups fed HFD or CD forming four study groups: (a) CD-CD, (b) CD-HFD, (c) HFD-CD and (d) HFD-HFD. The dams and offspring at the age of 37 and 18 weeks, respectively, were subjected to biochemical analysis of the blood and cytological analysis of the vaginal smears. Additionally body weight was recorded and body mass index (BMI) was calculated. RESULTS: The HFD-HFD group presented with highest levels of triglycerides and the CD-HFD with the highest levels of cholesterol. Therefore, triglyceride and cholesterol levels were significantly different among the groups (p = 0.001 and p = 0.002, respectively). Vaginal cytological smears analysis showed features of irregular phase interchanges or extended estrous phase in offspring of high-fat fed dams. CONCLUSION: Maternal HFD consumption predisposes offspring to increased risk of developing metabolic abnormalities and estrous disorders.

Proton pump (H+/K+-ATPase) expression in human larynx.

OBJECTIVE: The goal of our study was to investigate and to identify the existence of proton pump in different parts of larynx. The presence of acidic content in this area is known to be connected to several laryngeal diseases. It is mostly developed by upward recurrence of acidic gastric content, but there are some signs that the acid can be produced in the larynx as well, because of the proton pump activity in laryngeal mucosa. METHODS: The study was performed on two types of specimens: (1) 50 cadaver larynges and (2) 11 surgical larynges obtained after laryngectomy. Samples were taken from supraglottis, glottis and subglottic areas and immunohistochemistry for the beta subunit of the proton pump was done. RESULTS: The presence of proton pump was proved in seromucous glands in laryngeal supraglottic area, but it was also, for the first time, found in human chondrocytes in the thyroid and epiglottic cartilage. CONCLUSION: These new findings could encourage further research that would illuminate better the etiopathogenesis not only of laryngopharyngeal reflux, but also the pathophysiology of cartilaginous disorders.